Molecular Principal Chain: | Carbon Chain Polymer |
---|---|
Color: | Red |
Appearance: | Red Viscous Liquid |
Density: | 1.52-1.62 |
Viscosity: | 9-16 |
Glass Transition Temperature: | 70-85 |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Appearance | Main agent A | Red viscous liquid |
Curing agent B | Off-white viscous liquid | |
Density(25ºC) g/cm³ | Main agent A | 1.52-1.62 |
Curing agent B | 1.72-1.83 | |
Viscosity (40ºC, mPa.s) | Main agent A | 9-16 |
Curing agent B | 15-25 |
Tensile Strength (N/mm2) | 50-70 |
Elongation at break (%) | 1.8-2.5 |
Bending Strength (Mpa) | 105-125 |
Surface Strain (%) | 1.5-1.7 |
Fracture Ratio (J/m2) | 470-550 |
Glass Transition Temperature (ºC) | 70-85 |
Linear Expansion Coefficient(ppm/k, lower than the average of Tg ) | 38-47 |
Water Absorption(%, 100ºC/24h) | ≤0.5 |
Thermal Conductivity (W/mK) | 0.8-1.0 |
Insulation Strength (KV/mm) | 22-28 |
Dielectric Constant (50Hz) | ≤3.8 |
Volume Resistivity (Ω/cm) | ≥1.0x1016 |