Description
Good insulation performance, strong mechanical properties, good process performance, good surface gloss and fast curing speed.
Application
Suitable for dry-type transformer core coverage protection.
Characteristics
It has good insulation performance, strong mechanical properties, good process performance, good surface gloss and fast curing speed.
Test datas befiore curing,as bellow:
| Appearance |
Main agent A |
Black (Blue) viscous liquid |
| Curing agent B |
Brown (Light white) liquid |
| Density |
Main agent A |
800-1200 |
| Curing agent B |
15-35 |
| Viscosity |
Main agent A |
1000-3500 |
| Curing agent B |
15-35 |
Perfomance after curing:
| Water Absorption(%, 100ºC/24h) |
≤0.3 |
| Thermal Conductivity (W/mK) |
50-70 |
| Insulation Strength (KV/mm) |
1.8-2.5 |
| Bending Strength (Mpa) |
105-125 |
| Hardness (Shore D) |
1.5-1.7 |
| Dielectric Constant (50Hz) |
470-550 |
| Gel time (150ºC/s) |
170-210 |
| Volume Resistivity (Ω/cm) |
70-80 |
Ration
100:20
Curing conditions
It can be dried at 25ºC for 3-5 hours and completely cured within 24 hours.
Package
Component A: 25kg /barrel
Component B: 5kg /barrel
Storage conditions
The product should be sealed in its original packaging container and stored in a dry and ventilated place. In an environment of 18-40ºC, the shelf life is 6 months. If the shelf life is exceeded, analysis is required to determine whether it is still valid.
Due to storage conditions, this product may experience a small amount of precipitation during storage, which is a normal phenomenon. After stirring evenly, it can be used normally.
Attention
Due to the storage conditions, this product may experience a small amount of precipitation during storage, which is a normal phenomenon. After stirring evenly, it can be used normally.